Name: Flame Retardant UV-Resistant APG Epoxy Resin for High Dielectric Strength Electrical Insulation
Brand: Shanghai Wenyou Industry Co., Ltd.
SKU: LE-184/LH-8504
Price: 2.50 USD
Availability: InStock

Huis > producten > Elektrische epoxyhars >

Flame Retardant UV-Resistant APG Epoxy Resin for High Dielectric Strength Electrical Insulation

Flame retardant epoxy resin for electrical insulation

UV-resistant APG epoxy resin

High dielectric strength electrical epoxy resin

Plaats van herkomst:

China

Merknaam:

WENYOU

Certificering:

ISO/REACH/RoHS/SGS/UL

Modelnummer:

LE-184/LH-8504

Contacteer ons

Verzoek om een Citaat

Flame Retardant UV-Resistant APG Epoxy Resin for High Dielectric Strength Electrical Insulation

Productdetails

Impactsterkte:

10-18kJ/m²

Treksterkte:

60-85 MPa

Buigsterkte:

100-140 MPa

Glasovergang:

65-105°C

Afbraaksterkte:

25-30 kV/mm

Wateropname:

0,10-0,20%

Betaling & het Verschepen Termijnen

Min. bestelaantal

20 kg/emmer als monster

Prijs

Onderhandelbaar

Verpakking Details

20 kg/emmer, 220 kg/vat, 1200 kg/tank

Levertijd

7 tot 10 werkdagen

Betalingscondities

L/C, T/T, Western Union, MoneyGram

Levering vermogen

Er is veel grondstof op voorraad.

Verwante producten

Video

Flame Retardant Epoxy Resin Potting Compound with High Heat Resistance and Excellent Environmental Performance

Krijg Beste Prijs

Video

High Dielectric Strength Epoxy Resin with H-Class Thermal Stability and Superior Crack Resistance for Electrical Insulation

Krijg Beste Prijs

Flame Retardant UV-Resistant APG Epoxy Resin for High Dielectric Strength Electrical Insulation

Krijg Beste Prijs

Video

High Dielectric Strength Electrical Epoxy Resin for Medium & High Voltage Insulation with High Heat and Chemical Resistance

Krijg Beste Prijs

Contacteer ons

008618018933365

Elliot.yang@sh-wysy.com

86-21-64308192

Contact nu

Productomschrijving

Outdoor Epoxy Resin | UV-Resistant | APG/Vacuum Casting | High-Voltage Insulation

Product Specifications

Attribute	Value
Process	APG & Vacuum Casting
Impact Strength	10-18kJ/ M2
Temperature Resistance	High
Apply	high voltage transformer
Application	Electrical Insulation

Product Description

The LE-184/LH-8504 epoxy system is a weather-resistant, multi-component formulation engineered for outdoor high-voltage electrical insulation. Featuring modified BPA epoxy (LE-184), anhydride hardener (LH-8504), flexibilizer (LF-660), and accelerator (LZ-622), it delivers exceptional UV/erosion resistance, thermal shock stability, and superior dielectric performance. Ideal for APG or vacuum casting processes in harsh environments.

Key Features & Advantages

Feature	Advantage
UV & Weather Resistance	Withstands outdoor exposure, prevents erosion & yellowing
Flexibilizer LF-660 (0-20 pbw)	Enhances crack resistance under thermal cycling
Accelerator LZ-622 (0-0.4 pbw)	Speeds curing for high-volume production
APG & Vacuum Casting Compatible	Adapts to existing manufacturing setups
High Dielectric Strength	25-35 kV/mm (IEC 60243-1) for outdoor insulators
Low Water Absorption	0.10-0.20% (23°C/10d) ensures long-term integrity
Solvent-Free	Eco-friendly, low-VOC processing

Applications

Built for outdoor electrical components:

HV bushings, insulators & surge arresters
Transformer encapsulation
Outdoor switchgear (12-40.5 kV)
Solar/Wind energy infrastructure
Railway electrification components

Key Performance Data

Cured system: LE-184/LH-8504/Silica=100:90:350 | Cure: 140°C*2h + 130°C*10h

Mechanical & Thermal Properties

Property	Value	Standard
Tensile Strength	60-85 MPa	ISO 527
Flexural Strength	100-140 MPa	ISO 178
Impact Strength	8-16 kJ/m²	ISO 179
Glass Transition (Tg)	65-105°C	ISO 11357-2
Thermal Conductivity	0.7-0.9 W/m*K	ISO 8894-1
Decomposition Temp	>320°C	ASTM E2402

Electrical & Safety Properties

Property	Value	Standard
Breakdown Strength (3mm)	25-30 kV/mm	IEC 60243-1
HV Arc Resistance	185-195 sec	IEC 61621
Tracking Resistance	CTI>600 (Solution A/B)	IEC 60112
Electrolytic Corrosion	Grade A-1	IEC 60426
Flammability	HB Rating	UL94

Frequently Asked Questions (FAQ)

Q1: What's the role of LF-660 and LZ-622?

A: LF-660 (0-20 pbw) improves flexibility & crack resistance. LZ-622 (0-0.4 pbw) accelerates curing - critical for APG production.

Q2: How should I store components?

A: Store in sealed containers at 18-25°C. Shelf life: 24 months. Avoid moisture - hardener is humidity-sensitive.

Q3: What processing methods are supported?

A: Optimized for:
APG: Mold temp 130-150°C | Gel time 10-50 min
Vacuum Casting: Cure 80-100°C | Gel time 3-6h
Post-cure: 130-140°C*6-10h for all methods

Q4: How is filler pre-treated for HV applications?

A: Silica filler must be pre-dried (moisture ≤0.2%). Use thin-film degassing mixers for consistent dispersion.

Q5: Is this system suitable for coastal environments?

A: Yes! UV resistance + low water absorption (0.10-0.20%) prevents salt corrosion & tracking.

Taggen：

Flame Retardant UV-Resistant APG Epoxy Resin for High Dielectric Strength Electrical Insulation

Flame retardant epoxy resin for electrical insulation

UV-resistant APG epoxy resin

High dielectric strength electrical epoxy resin

Flame Retardant Epoxy Resin Potting Compound with High Heat Resistance and Excellent Environmental Performance

High Dielectric Strength Epoxy Resin with H-Class Thermal Stability and Superior Crack Resistance for Electrical Insulation

Flame Retardant UV-Resistant APG Epoxy Resin for High Dielectric Strength Electrical Insulation

High Dielectric Strength Electrical Epoxy Resin for Medium & High Voltage Insulation with High Heat and Chemical Resistance

vloeibare gietende epoxyhars

bus hoge viscositeit epoxyhars

elektrische epoxyhars lichtgeel